Hot Rolled Steel

                Our hot rolled steels are produced to meet the chemistry and dimensional requirements of our customers.

                Consistency from coil to coil is maintained by applying ladle metallurgy and continuous casting to molten steel, and rolling on a hot strip mill that features advanced process controls. For specific applications a subsequent pickling operation helps produce excellent strip surfaces.

                Contact Our Sales Team

                We're here to answer your questions.

                CONTACT NOW

                Product Applications

                Available Grades

                Commercial Steel (CS)

                Drawing Steel (DS)

                High Strength Low Alloy Steel (HSLAS)

                Press Hardenable Steel (PHS)

                Product Details

                Product Features


                Hot rolled steels can be used to produce parts containing simple bends as well as drawn parts.

                THICKNESS CONTROL

                An automatic gauge control system assures excellent thickness control.


                Hot rolled steels can be joined using accepted welding practices.


                A wide variety of hot rolled steels are available in thicknesses of 0.071 – 0.525 in. (1.80 – 13.34 mm) and widths of 30 – 80 in. (1016 – 2032 mm), depending on thickness.


                We produce top quality products by utilizing modern, well-maintained equipment. This begins with quality slabs, produced by continuous casting, creating a uniform chemistry for hot rolled steel. The hot strip mill is designed to produce consistent surface quality, uniform mechanical properties, and consistent thickness and crown. Walking beam furnaces minimize surface damage during slab reheating. Scale breakers remove heavy furnace scale and provide a uniform surface for rolling. Strip temperatures are controlled at critical points during rolling to produce the desired mechanical properties. The finishing mill produces excellent thickness and crown controls. Finally, pickling can be used to remove the oxide that forms during cooling.

                Joining Systems

                Most hot rolled steels can be readily fabricated using a variety of welding and joining processes. This is largely due to the low carbon and alloy content, strength levels, and low impurity characteristics. Depending on gauge, surface conditions (pickled or unpickled) and joint design, suitable processes include arc welding, resistance welding, brazing, and soldering. Resistance spot/seam/projection welding, soldering, and brazing normally are incompatible with unpickled hot rolled steel. However, many arc welding processes, that utilize consumable filler materials, can be used successfully on unpickled (referred to as “black”) hot rolled steel. Additional factors must be considered when welding medium and high strength hot rolled grades. Technical assistance is available to select appropriate welding techniques for these steels.

                Formability and Mechanical Properties

                COMMERCIAL STEEL (CS)

                Commercial Steel (CS Type B) should be used for moderate forming or bending applications. Commercial Steel products are produced from aluminum-killed, continuously cast slabs and, unless otherwise specified, have a carbon content of less than 0.15%.

                DRAWING STEEL (DS)

                For more severe forming applications, Drawing Steel (DS Type B) can be ordered. Drawing Steel has a controlled carbon content of less than 0.08%. For more formability and to help minimize coil breaks, DS with boron can be ordered.


                HSLAS is intended for applications where greater strength or weight savings are important.

                The increased strength of HSLAS is achieved from niobium or vanadium additions. Two classes are available (Class 1 and Class 2).

                STRUCTURAL STEEL (SS)

                Structural Steel (SS) is available for structural purposes where specific mechanical properties are required. Strength is achieved primarily by carbon and manganese additions.


                Press hardenable steel, commonly referred to as 22MnB5 or 15B22, is available as hot rolled black or pickled and oiled. This material is used in hot stamping applications to achieve final ultimate tensile strength approaching 1500 MPa.

                Contact Us

                Contact Us

                Request Information

                Our team or one of our subsidiaries will be in touch promptly to address your inquiry.

                Additional Information

                To provide a timely response, please add additional details on size, grade and volume desired.

                What Are You Interested In?

                Please check all that apply

                Are you an international customer?

                Click here for Privacy Policy Statement.

                Contact Us By Phone

                Customer Service


                Corporate Headquarters

                Media Relations

                Lisa H. Jester

                Corporate Manager, Communications and Public Relations

                Investor Relations

                Jaime Vasquez

                Vice President, Finance and Chief Financial Officer

                Christopher J. Ross

                Vice President and Treasurer

                Douglas O. Mitterholzer

                General Manager, Investor Relations and Assistant Treasurer